The effect of hexagonal boron nitride nanopowders addition on the mechanical behaviors of basalt fabric reinforced composites

The purpose of this paper is to investigate the effect of doping element on the structural, thermal properties, mechanical performance and the failure mechanism of hexagonal nano boron nitride (h-BN)-reinforced basalt fabric (BF)/epoxy composites produced by hand lay-up and vacuum bagging technique. h-BN particles doped to composite materials increased the tensile, bending and impact strength of the composite at certain rates while 1 Wt. % h- BN addition shows the highest tensile and flexural strength.

The epoxy resin was doped with h-BN nanopowder at the certain rates (0, 1, 2 and 4 Wt.%) and the epoxy: hardener ratios used in the study were selected as 80%: 20% by weight. Then, with the aid of a roller by hand lay-up method, a mixture of epoxy + hardeners containing nanoparticles and nanoparticle-free were fed onto BFs, 12 layers of each dimension 30 cm × 30 cm. The surplus epoxy resin was moved away from the composite sheets using the vacuum bagging process and left to cure at room temperature for 24 h. ASTM D3039 for tensile, D7264 for three-point bending and D256 for Izod impact test were performed for the mechanical tests. After the tensile test, the morphologies of the fracture surface were examined with a stereomicroscope and various failure mechanisms are highlighted.

In this study, a series of basalt/epoxy composites with h-BN nanopowders have been prepared to identify the effect of filler ratio on mechanical properties. It has been known from the results of mechanical experiments that the addition of h-BN improves the mechanical performance of materials at a certain rate. The tensile and flexural strengths of h-BN doped composites, increase for concentrations of 1 Wt.% h-BN, but decrease with the increasing content of it. The basalt/epoxy resin composite with higher mechanical properties could be a potential material in the automotive and aerospace industries.

The aim of this study is to contribute to literature within the context of this new combination of composites and their mechanical properties, failure mechanisms. It presents detailed characterization of each composite by using X-ray differaction (XRD), differential scanning calorimetry (DSC), fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy.