The enthalpy and heat capacity of solid and liquid Mg2Ca intermetallic alloy were measured by massive high-temperature isothermal drop calorimeter over the temperature range of 298.15–1177 K. The estimated errors in the data on enthalpy and heat capacity were 0.2 % and 2 %, respectively. The fusion enthalpy of the Mg2Ca intermetallic alloy was determined to be 483 ± 3 J/g. The heat capacity of the Mg2Ca melt was shown to be constant in the range of 993.2–1177 K. A comparison of the obtained results with literature data has been carried out.
References
C. Zehnder, K. Czerwinski, K.D. Molodov, S. Sandlöbes-Haut, J.S.L. Gibson, and S. Korte-Kerzel, Plastic deformation of single crystalline C14 Mg2Ca Laves phase at room temperature, Mater. Sci. and Engng: A., 2019, Vol. 759, P. 754–761.
Z. Li, X. Gu, S. Lou, and Y. Zheng, The development of binary Mg–Ca alloys for use as biodegradable materials within bone, Biomaterials, 2008, Vol. 29, No. 10, P. 1329–1344.
N. Terashita and E. Akiba, Hydrogenation properties of CaMg2 based alloys, Mater. Trans., 2004, Vol. 45, No. 8, P. 2594–2597.
A.A. Nayeb-Hashemi and J.B. Clark, The Ca–Mg (Calcium–Magnesium) system, Bull. Alloy Phase Diagrams, 1987, Vol. 8, No. 1, P. 58–65.
J.E. Davison, A measurement of the heat capacity of CaMg2 and a calculation of the cohesive energy of CaMg2, Iowa State Univ. Sci. and Technology, 1966.
R. Agarwa, J.J. Lee, H.L. Lukas, and F. Sommer, Calorimetric measurements and thermodynamic optimization of the Ca-Mg system, Inter. J. Mater. Res., 1995, Vol. 86, No. 2, P. 103–108.
R.N. Abdullaev, A.Sh. Agazhanov, A.R. Khairulin, D.A. Samoshkin, and S.V. Stankus, Thermophysical properties of magnesium in solid and liquid states, J. Engng Thermophys., 2022, Vol. 31, No. 3, P. 384–401.
R.N. Abdullaev, R.A. Khairulin, A.Sh. Agazhanov, A.R. Khairulin, Yu.M. Kozlovskii, and D.A. Samoshkin, Density, thermal expansion, enthalpy, heat capacity and thermal conductivity of calcium in the temperature range 720–1290 K, Rus. J. Inorg. Chem., 2023, Vol. 68, No. 2, P. 158–166.
J. Bohdansky and H.E.J. Schins, Surface tension and density of the liquid earth alkaline metals Mg, Ca, Sr, Ba, J. Inorg. Nucl. Chem., 1968, Vol. 30, No. 9, P. 2331–2337.
S.V. Stankus, I.V. Savchenko, and O.S. Yatsuk, A high-temperature drop calorimeter for studying substances and materials in the solid and liquid states, Instruments and Experimental Techniques, 2017, Vol. 60, No. 4, P. 608–613.
D.A. Ditmars and T.B. Douglas, Measurement of the relative enthalpy of pure α-Al2O3 (NBS Heat Capacity and Enthalpy Standard Reference Material No. 720) from 273 to 1173 K, J. Res. Natl. Bur. Stand. Sec. A, Phys. and Chem., 1971, Vol. 75, No. 5, P. 401–420.
J.M. Newhouse, S. Poizeau, H. Kim, B.L. Spatocco, and D.R. Sadoway, Thermodynamic properties of calcium-magnesium alloys determined by emf measurements, Electrochem. Acta, 2013, Vol. 91, P. 293–301.
Author information
Authors and Affiliations
Corresponding author
Additional information
This work was financially supported by the Russian Science Foundation (Grant No. 20-79-10025).
Rights and permissions
About this article
Cite this article
Abdullaev, R.N., Khairulin, A.R. & Agazhanov, A.S. Caloric properties of the Mg2Ca intermetallic compound in solid and liquid states. Thermophys. Aeromech. 30, 553–556 (2023). https://doi.org/10.1134/S0869864323030137
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0869864323030137