Preparation and Characterization of Crosslinking Polyacrylate Latex Prepared by Soap-Free Emulsion Polymerization

  • FUNCTIONAL POLYMERS
  • Published:
Polymer Science, Series B Aims and scope Submit manuscript

Abstract

The cross-linking acrylic polymer latex based on methyl methacrylate, butyl acrylate, hydroxyethyl methacrylate, and hydroxyethyl acryloylurea was prepared by soap-free emulsion polymerization with sodium 2-acrylamido-2-methylpropanesulfonate and allyloxy alkyl polyoxyethylene ether ammonium sulfate (SR-10) used as the reactive emulsifiers. Glass transition temperature of the latex film prepared is 20°C. The average particle size of the latex is 64 nm and its dispersion index is 0.085. The optimum conditions of preparing the latex were found. In comparison with the conventional latex, the heat and water resistance of the resultant latex have been improved.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1.
Fig. 2.
Fig. 3.
Fig. 4.
Fig. 5.
Fig. 6.

REFERENCES

  1. J. Machotová, E. Černošková, J. Honzíček, and J. Šňupárek, Prog. Org. Coat. 120, 266 (2018).

    Article  Google Scholar 

  2. W. Xu, Q. F. An, L. F. Hao, D. Zhang, and M. Zhang, Fiber Polym. 15, 457 (2014).

    Article  CAS  Google Scholar 

  3. J. Lin, C. Zheng, M. N. Zhu, Y. Z. Chen, P. P. Lu, Q. Liu, X. F. Cai, J. W. Zhuang, X. M. Cai, L. P. Liao, G. Y. Yuan, and C. L. Xu, Polym. Adv. Technol. 26, 68 (2014).

    Article  Google Scholar 

  4. C. Fang, Q. M. Yan, Z. Z. Liu, Y. F. Lu, and Z. X. Lin, Int. J. Adhes. Adhes. 84, 387 (2018).

    Article  CAS  Google Scholar 

  5. M. Haruki, Y. Kodama, K. Tachimori, S. I. Kihara, and S. Takishima, J. Appl. Polym. Sci. 133, 1 (2016).

    Google Scholar 

  6. C. Y. Jiao, Q. Shao, M. Y. Wu, B. Zheng, Z. Guo, J. M. Yi, J. X. Zhang, J. Lin, S. D. Wu, M. Y. Dong, and Z. H. Guo, Polymer 190, 196 (2020).

    Article  Google Scholar 

  7. C. L. Zhou, S. P. Xu, P. H. Pi, J. Cheng, L. Wang, J. X. Yang, and X. F. Wen, Prog. Org. Coat. 121, 30 (2018),

    Article  CAS  Google Scholar 

  8. O. D. Lewis, G. W. Critchlow, G. D. Wilcox, A. Dezeeuw, and J. Sander, Prog. Org. Coat. 73, 88 (2012).

    Article  CAS  Google Scholar 

  9. M. S. Shin, Y. H. Lee, M. M. Rahman, and H. D. Kim, Polymer 54, 4873 (2013).

    Article  CAS  Google Scholar 

  10. J. Wang, X. R. Zeng, and H. Q. Li, J. Coat. Technol. Res. 7, 469 (2010).

    Article  CAS  Google Scholar 

  11. M. Ishihara, T. Kaeda, and T. Sasaki, e-Polymers 20, 254 (2020).

  12. S. Q. Wu, B. Wang, Y. H. Zhang, and P. X. He, Adhesion 39, 40 (2018).

    Google Scholar 

  13. C. F. Zhang, T. T. Xu, Z. B. Bao, Z. R. Fu, and L. J. Chen, J. Adhes. Sci. Technol. 31, 1658 (2016).

    Article  Google Scholar 

  14. Y. J. Zhu and G. F. Wu, Colloid Polym. Sci. 299, 73 (2021).

    Article  CAS  Google Scholar 

  15. T. T. Shao, X. L. Chen, and L. J. Chen, Pigm. Resin Technol. 51, 265 (2022).

    Article  CAS  Google Scholar 

  16. X. M. Wang, Z. B. Bao, and L. J. Chen, J. Polym. Mater. 33, 685 (2017).

    Google Scholar 

  17. L. J. Chen, Z. B. Bao, Z. R. Fu, and W. Li, Colloid J. 77, 374 (2015).

    Article  CAS  Google Scholar 

  18. L. J. Chen, Chin. Chem. Lett. 22, 1249 (2011).

    CAS  Google Scholar 

  19. L. J. Chen and F. Q. Wu, J. Appl. Polym. Sci. 123, 1997 (2012).

    Article  CAS  Google Scholar 

  20. J. T. Xu, V. L. Dimonie, E. D. Sudol, O. L. Shaffer, and M. S. El-Aasser, J. Appl. Polym. Sci. 69, 977 (1998).

    Article  CAS  Google Scholar 

Download references

Funding

This work was supported by ongoing institutional funding. No additional grants to carry out or direct this particular research were obtained.

Author information

Authors and Affiliations

  1. School of Chemical Engineering, Zhejiang University of Technology, 310032, Hangzhou, China

    Lijun Chen &  Zheqing Gong

Authors
  1. Lijun Chen
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Zheqing Gong
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Lijun Chen.

Ethics declarations

The authors of this work declare that they have no conflicts of interest.

Additional information

Publisher’s Note.

Pleiades Publishing remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Lijun Chen, Zheqing Gong Preparation and Characterization of Crosslinking Polyacrylate Latex Prepared by Soap-Free Emulsion Polymerization. Polym. Sci. Ser. B 65, 836–841 (2023). https://doi.org/10.1134/S1560090424600074

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1134/S1560090424600074

Search

Navigation